Duplex Steel Reducer Tee ASTM A815 WP WX S32750 Sewage Treatment Pipeline
Overwiew
S32750 stainless steel has high strength, corrosion resistance and stress corrosion cracking resistance, and is suitable for high strength and corrosion resistant structural parts and components in the marine, chemical, oil and gas industries. The material's resistance to chloride ion stress corrosion cracking is better than other stainless steels, so it is suitable for seawater environments.
S32750 stainless steel can be subjected to heat treatment processes, including solid solution and water quenching. The solid solution temperature is 1020-1100 ℃, holding time is 1-2 hours; water quenching followed by annealing treatment, annealing temperature is 700-800 ℃, holding time is 2-4 hours.
Mechanical Properties of ASTM A815 UNS S32750 Reducer Tee
| Grades | Density (g/cm 3) | Density (lb/in 3) | Melting Point (°C) | Melting Point (°F) |
| UNS S32750 Pipe Fittings | 7.8 | 0.281 | 1350 | 2460 |
Equivalent Grades of ASTM A815 UNS S32750 Reducer Tee
Chemical Composition of Duplex Steel Reducer Tee
| EL. | S31803 | S32205 | S32750 | S32760 |
| C | ≤0.030 | ≤0.030 | ≤0.030 | ≤0.030 |
| Mn | ≤2.00 | ≤2.00 | ≤1.20 | ≤1.00 |
| P | ≤0.030 | ≤0.030 | ≤0.035 | ≤0.030 |
| S | ≤0.020 | ≤0.020 | ≤0.020 | ≤0.010 |
| Si | ≤1.00 | ≤1.00 | ≤0.80 | ≤1.00 |
| Ni | 4.5-6.5 | 4.5-6.5 | 6.0-8.0 | 6.0-8.0 |
| Cr | 21.0-23.0 | 22.0-23.0 | 24.0-26.0 | 24.0-26.0 |
| Mo | 2.5-3.5 | 3.0-3.5 | 3.0-5.0 | 3.0-4.0 |
| Cu | - | - | ≤0.50 | 0.50-1.00 |
| N | 0.08-0.20 | 0.14-0.20 | 0.24-0.32 | 0.20-0.30 |
| W | - | - | - | 0.50-1.00 |
Tensile and hardness requirements of Duplex Steel Reducer Tee
| Item | S31803 | S32205 | S32750 | S32760 |
Yield Strength
min. MPa [ksi] | 450 [65] | 450 [65] | 550 [80] | 550 [80] |
Tensile Strength
min. MPa [ksi] | 620 [90] | 655 [95] | 800 [116] | 750 [109] |
Elongation in
2" min. % | 20.0 | 20.0 | 15.0 | 25.0 |
| HBW, max | 290 | 290 | 310 | 270 |
Characteristic of Duplex Steel Pipe fitting
1. Yield strength is more than twice as high as ordinary austenitic stainless steel, and has sufficient plastic toughness for molding.
2. Excellent resistance to stress corrosion rupture, especially in the chlorine ion environment.
3. Super duplex steel has a very high corrosion resistance, in some media, such as acetic acid, formic acid, and even higher can replace high-alloy austenitic stainless steel, and even corrosion-resistant alloys.
4. Good resistance to localized corrosion, and the alloy content of austenitic stainless steel, compared to its resistance to wear corrosion and fatigue corrosion than austenitic
Application
Sewage treatment pipeline
Oil refining
chemical fertilizer
Marine environments
seawater resistance quipment
|
|